Picture of Plastic Gears-LogoPlastic Gears-Yeh Der


Home
Plastic Gear
Worm plastic Gears
Helical Plastic Gears
Pinion Plastic Gears
Spur Plastic Gears
Bevel Plastic Gears
Other Plastic Gears
Process
Powder Metallurgy Gear
  Products
Process
Production Equipment
Inspection Equipment
Gearbox
Prototype
Injection Molding
  Personnel
Tooling
Software
΅@ Example 01
΅@ Example 02
Equipment
Molding
΅@ Insert Molding
Products
΅@ Automotive
΅@ Computer
΅@ Home Appliances
΅@ Heath Care
΅@ Remote Control
΅@ Meter
΅@ Decoration
Plastic Material
Assembly
About Us
Contact Us
Sitemap
¤¤¤εΊτ­¶
Catalogue Download
 

Plastic Material PC
Plastic Material PC

 
PC (Polycarbonate)


Typical Applications


Electronic and business equipment (computer parts, connectors, etc.), appliances (food processors, refrigerator drawers, etc.), transportation (head lights, tail lights, instrument panels, etc.)

Injection Molding Processing Conditions

Drying

PC resins are hygroscopic and pre-drying is important. Recommended drying conditions are 100 - 120 C (212 - 248 F) for 3 to 4 hours. Moisture content must be less than 0.02% prior to processing. 

Melt Temperature

260 - 340 C (500 - 644 F); higher range for low MFR resins and vice-versa 

Mold Temperature 

70 - 120 C (158 - 248 F); higher range for low MFR resins and vice-versa 

Fill Pressure

As high as possible for rapid molding 

Injection Speed

Slow injection speeds when small or edge gates are used; high speeds for other types of gates 


Chemical and Physical Properties


Polycarbonate is a polyester of carbonic acid. All general-purpose polycarbonates are based on bisphenol A. The bisphenol A component of the molecule contributes to the high glass transition temperature (150 C / 302 F). The rotational mobility of the carbonyl group within the molecule contributes to the high ductility and toughness of the resin.

PC is an amorphous engineering resin with exceptionally good impact strength, heat resistance, clarity, sterilizability, flame retardancy, and stain resistance. The notched Izod impact strength of PC is very high and mold shrinkage is low and consistent (.1 -.2 mm/mm).

High molecular weight PCs (which translate to low melt flow rate) have higher mechanical properties, but processibility of such resins becomes difficult. The type of PC chosen for a particular application should be based on the desired criteria (for high impact properties, use a low-MFR PC; conversely, for optimal processibility, use a high-MFR PC).

The melt viscosities are typically Newtonian up to shear rates of 1000 1/s and decrease beyond that. The Heat Deflection Temperature Under Load is typically between 130 -140 C (266 - 284 F) and the Vicat Softening Point is typically around 155 C (311 F).

Major Manufacturers

Dow Chemical (Caliber), GE Plastics (Lexan), Bayer (Apec, Macrolon), DSM (Xantar), LNP (Lurbricomp, Thermocomp), Mitsubushi Engineering Plastics (Novarex), Teijin Chemical (Panlite).