Picture of Plastic Gears-LogoPlastic Gears-Yeh Der

Plastic Gear
Worm plastic Gears
Helical Plastic Gears
Pinion Plastic Gears
Spur Plastic Gears
Bevel Plastic Gears
Other Plastic Gears
Powder Metallurgy Gear
Production Equipment
Inspection Equipment
Injection Molding
¡@ Example 01
¡@ Example 02
¡@ Insert Molding
¡@ Automotive
¡@ Computer
¡@ Home Appliances
¡@ Heath Care
¡@ Remote Control
¡@ Meter
¡@ Decoration
Plastic Material
About Us
Contact Us
Catalogue Download

Plastic Material PP
Plastic Material PP

PP (Polypropylene)


Automotive (mostly mineral-filled PP is used: dashboard components, ductwork, fans, and some under-hood components), appliances (doorliners for dishwashers, ductwork for dryers, wash racks and lids for clothes washers, refrigerator liners, etc), consumer products (lawn/garden furniture, components of lawn mowers, sprinklers, etc).

Injection Moulding Processing Conditions:

Drying¡GNot normally necessary if proper storage is used.

Melt Temperature¡G220-275 ¢J(not to exceed 275 ¢J).

Mould Temperature¡G40-80 ¢J (suggested: 50 ¢J). The crystallinity level is
determined by the mould temperature.

Injection Pressure¡GUp to 180 MPa.

Packing Pressure¡G60-80% of injection pressure (up to 150 MPa).

Injection Speed¡GTypically, fast injection speeds are used to minimize
internal stresses; if surface defects occur, slow speed molding at a higher temperature is preferred. Machines capable of providing profiled speed is highly recommended.

Runners and Gates

In the case of cold runners, typical diameters range from 4-7 mm. Full round sprues and runners are recommended. All types of gates can be used. Typical pin gate diameters range from 1-1.5 mm, but diameters as low as 0.7 mm may be used. In case of edge gating, the minimum gate depth should behalf the wall thickness and the width should be at least double the thickness. Hot runners can readily be used for moulding PP.

Chemical and Physical Properties

PP is produced by the polymerisation of propylene using stereospecific catalysts. Mainly, isotactic PP is produced (the methyl groups lie on one side of the carbon chain). This linear plastic is semicrystalline because of ordered molecular structure. It is stiffer than PE and has a higher melting point. The PP homopolymer becomes very brittle at temperatures higher than 0oC and for this reason; many commercially available grades are random copolymers with 1-4% ethylene or block copolymers with higher ethylene content. Copolymers have a lower heat distortion temperature (approximately 100 oC), less clarity, gloss, and rigidity, but greater impact strength. The material becomes tougher as the ratio of ethylene increases. The Vicat softening point is approximately 150oC. Because of high levels of crystallinity, the surface hardness and scratch resistance is higher for these materials.

PP does not have environmental stress cracking problems. PP is usually modified by addition of glass fibers, mineral fillers, or thermoplastic rubbers. The MFR of PP ranges from 1 to 40; lower MFR materials have better impact strength but lower tensile strength. The copolymer is tougher than the homopolymer of the same MFR. The viscosity is more shear and temperature sensitive than PE.
Due to crystallinity, the shrinkage is relatively high (order of 0.019-0.025 mm/mm or 1.8-2.5%). The shrinkage is more uniform than PE-HD (the difference in flow and cross-flow shrinkage is typically less than 0.2%). Addition of 30% glass reduces the shrinkage to approximately 0.7%.

Both homopolymer and copolymer PP offer excellent resistance to moisture and good chemical resistance to acids, alkalis, and solvents. However, it is not resistant to aromatic hydrocarbons such as benzene, and chlorinated hydrocarbons such as carbon tetrachloride. It is not as resistant to oxidation at high temperatures as PE.